The use of aluminum profiles can now be very common. Whether in industrial production and manufacturing, or daily consumption can see aluminum material. But although the aluminum profile has many advantages, but if you do not pay attention to it will also be easily damaged. Next, Shenghai Aluminum will introduce to you the cause of aluminum profile damage and what the solution is.
The main reasons for aluminum profile damage are:
1. The ingot surface is attached to sundries or ingot composition segregation. Ingot surface existing number of segregation to content and ingot casting and homogenizing treatment or homogenization treatment effect is bad, ingot exist within a certain number of hard metal particles, we think metal in the process of extrusion through the work zone, the segregation to objects or hard metal particles adhere to the work surface with or cause damage to work with.
2. We think that there are sundry in the mold cavity or working belt, and the hardness of the mold working belt is low, so that the surface of the working belt is injured and scratched during extrusion.
3. We think that the discharge track or bed on the bare metal or graphite strip within the hard inclusions, when the contact with the profile of the profile surface caused scratches.
4. There is a fork in the material rod will profile from the discharge track to the bed, because the speed is too fast caused by the profile collision. In addition, we think that the aluminum profile in the process of transportation between the friction or extrusion will also be damaged.
Shenghai Aluminum is a manufacturer and sales of high strength industrial aluminum alloy profiles, accessories and conveyor equipment (chain plate conveyor, belt conveyor). As the pioneer of aluminum alloy frame assembly technology in China, Shenghai Aluminum always adheres to the principle of focus and integrity and actively serves our customers.
The above is Shenghai Aluminum for your in-depth analysis of the aluminum profile damage, I hope it will be of some help to you, if you want to know other words, please contact us！